Titanium Flange Manufacturer www.titaniuminfogroup.com forniture Titanium Weld Neck Flange (Titanium WN Flange), Titanium Long Welding Neck Flange (Titanium LWN Flange), Flangia di giunzione in titanio (Titanium LJ Flange), Flangia cieca in titanio/Blank Flange (Titanium BL Flange), Titanium Slip On Flange (Titanium SO Flange), Titanium Thread Flange (Titanium TH Flange), Flangia a saldare in titanio (Titanium SW Flange), Titanium Reducing Flange, Flangia dell'orifizio in titanio, Titanium Anchor Flange, Flangia cieca per occhiali in titanio (Titanium Figue 8 Flange), Anello distanziatore in titanio/flangia a forcella etc.
Standards of Titanium Flange
- ANSI/ASME Standard: ANSI B16.5, ANSI B16.47 Series A & B, MSS-SP-44, API 605, API6A in class 150 to 2500;
- AWWA C207 flanges in Class B, Class D, Class E, Class F, Ring, Blind & Hub;
- European DIN, UNI, EN 1092-1, BS 4504, ISO, NS, NFE29203 flanges in Pressure PN6 to PN100;
- Japanese JIS B2220 & Korean KS B1503 flanges in pressure 5K to 40K;
- Russian GOST 12820-80, GOST 12821-80, GOST 12815-80 in pressure PN0.6MPa to PN10MPa;
- South African SABS 1123 / SANS 1123 in Class 600kPa to 4000kPa.
Materials of Titanio Flange
Titanium Grade 1-4 is pure Titanium, the other grades are alloys. Pure Titanium is used due to its high corrosion resistance, the alloys because of the extremely high strength to weight ratio.
Grade 1. Pure Titanium, relatively low strength and high ductility.
Grade 2. The pure titanium most used. The best combination of strength, ductility and weldability.
Grade 3. High strength Titanium, used for Matrix-plates in shell and tube heat exchangers.
Grade 5. The most manufactured titanium alloy. Exceedingly high strength. High heat resistance.
Grade 7. Superior corrosion resistance in reducing and oxidizing environments.
Grade 9. Very high strength and corrosion resistance..
Grade 12. Better heat resistance than pure Titanium. Applications as for Grade 7 and Grade 11.
Grade 23. Titanium-6Aluminum-4Vanadium ELI (Extra Low Interstitial) Alloy for surgical implant Applications.
Chemical, Physical And Mechanical Properties |
|||||||
Composizione chimica |
ASTM Grade |
||||||
(Max. Values) |
1 |
2 |
5 |
7 |
9 |
12 |
23 |
N, Nitrogen |
0,03 |
0,03 |
0,05 |
0,03 |
0,02 |
0,03 |
0,03 |
C, Carbon |
0,1 |
0,1 |
0,1 |
0,1 |
0,05 |
0,08 |
0,08 |
H, Hydrogen |
0,015 |
0,015 |
0,0125 |
0,015 |
0,013 |
0,015 |
0,0125 |
Fe, Iron |
0,2 |
0,3 |
0,4 |
0,3 |
0,25 |
0,3 |
0,25 |
O, Oxygen |
0,18 |
0,25 |
0,20 |
0,25 |
0,12 |
0,25 |
0.13 |
Pd, Palladium |
0,12-0,25 |
||||||
Al, Aluminum |
5,5-6,75 |
2,5-3,5 |
5,5-6.5 |
||||
Mo, Molybdenum |
0,2-0,4 |
||||||
V, Vanadium |
3,5-4,5 |
2,0-3,0 |
3,5-4,5 |
||||
Ni, Nickel |
0,6-0,9 |
||||||
Ti, Titanium |
Bal. |
Bal. |
Bal. |
Bal. |
Bal. |
Bal. |
Bal. |
MECHANICAL PROPERTIES |
|||||||
Tensile strength, min (Mpa) |
240,00 |
345,00 |
895,00 |
345,00 |
620,00 |
483,00 |
828,00 |
Yield strength, 0,2% Offset, min (Mpa) |
170,00 |
275,00 |
825,00 |
275,00 |
483,00 |
345,00 |
759,00 |
Elongation (in 4D, min, %) |
24,00 |
20,00 |
10,00 |
20,00 |
15,00 |
18,00 |
10,00 |
Reduction of Area, min, % |
30,00 |
30,00 |
25,00 |
30,00 |
25,00 |
25,00 |
15,00 |
Hardness * Interpolated |
Rb70 |
Rb80 |
Rc36 |
Rb80 |
Rc28 |
Rc17* |
Tipo di faccia della flangia: Flate Face (FF), Raised Face (RF), Ring Type Joint (RTJ)
Flange Norminal Diameter Range: 1/2” – 96”, DN15-DN2000
Normail Pressure Range: 150# – 2500# (PN6 – PN40)